Investigation of microstructure in hot-pressed Nb–23Ti–15Al alloy

Microstructure of hot-pressed Nb–23Ti–15Al alloy has been systematically investigated, with emphasis on the characterization of Ti(O, C) phase. The microstructure and composition of Nb–23Ti–15Al alloy were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and electron probe microanalysis (EPMA).

The results indicate the presence of β, δ and Ti(O, C) phases in the alloy. The β phase exhibits as large irregular blocks, while the δ phase presents as small equiaxed particles linked together around β blocks. Ordering of β phase is shown by related selected area electronic diffraction (SAED) patterns and dark-field micrograph.

The Ti(O, C), a solid-solution of TiO or TiC, is characterized for the first time in Nb–Ti–Al alloy. The Ti(O, C) has a face-centered cubic (FCC) structure and a moderate lattice parameter between that of TiO and TiC. Two different morphologies of Ti(O, C) are observed in the alloy: large cobblestone-like aggregated particles and small dispersive particles.

The formation of Ti(O, C) phase can potentially increase high-temperature strength of Nb–Ti–Al alloy.