Residual stresses in Al2O3/Y-TZP Ceramic Laminates Fabricated by Tape and Slip Casting
Universidad Politécnica de Madrid, Departamento de Ciencia de Materiales, E.T.S. Ingenieros Caminos, Canales y Puertos, Profesor Aranguren s/n, Madrid, 280801
Instituto de Cerámica y Vidrio, CSIC , Campus de Cantoblanco , Calle Kelsen s/n, Madrid , 280492
CSIC-Universidad de Zaragoza, Instituto de Ciencia de Materiales de Aragón, Departamento de Ciencia de Materiales e Ingeniería Metalúrgica, C/Pedro Cerbuna 12, Zaragoza, 500183
Università degli studi di Bari, Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR , Via E. Orabona 4, Bari, 701264
Residual stress profiles were measured by neutron diffraction in Al2O3/Y-TZP ceramic composites containing 5 and 40 vol.% Y-TZP fabricated by conventional slip casting and by a novel tape casting route. Residual stresses in the zirconia are tensile and increase as its volume fraction decreases. For the alumina matrix, residual stress is compressive and increases with the zirconia volume fraction.
In the composite with 5 vol.% zirconia, the processing route does not have an influence on residual stresses. However, in the composite with 40 vol.% zirconia, residual stresses are different in the samples obtained by both processing routes.
Language: | English |
---|---|
Publisher: | Trans Tech Publications Ltd |
Year: | 2008 |
Pages: | 327-332 |
ISSN: | 16629752 and 02555476 |
Types: | Journal article |
DOI: | 10.4028/www.scientific.net/MSF.571-572.327 |