Journal article
Fabrication of a Textured Non-Magnetic Ni-12at.%V Alloy Substrate for Coated Conductors
Beijing University of Technology1
Nano-Microstructures in Materials, Materials Research Division, Risø National Laboratory for Sustainable Energy, Technical University of Denmark2
Materials Research Division, Risø National Laboratory for Sustainable Energy, Technical University of Denmark3
Risø National Laboratory for Sustainable Energy, Technical University of Denmark4
Ni-12at.%V alloy is a promising candidate for non-magnetic cube textured metallic substrates used for high temperature coated conductors. In this work, a textured Ni-12at.%V substrate has been fabricated by powder metallurgy route. After cold rolling and recrystallization annealing, a cube texture content as high as 99% $(
Language: | English |
---|---|
Publisher: | IEEE |
Year: | 2011 |
Pages: | 2973-2976 |
ISSN: | 15582515 , 10518223 and 23787074 |
Types: | Journal article |
DOI: | 10.1109/TASC.2010.2090631 |
ORCIDs: | Grivel, Jean-Claude |
Annealing Coated conductor Conductors Curie temperature FWHM values Ni alloy NiV Nickel Substrates Superconducting epitaxial layers Yttrium barium copper oxide coated conductors cold rolling cube texture grain boundaries low angle grain boundary fraction magnetization loss microhardness microhardness measurement nickel alloys powder metallurgy recrystallisation annealing recrystallization annealing rocking curve surface texture tape textured nonmagnetic alloy substrate vanadium alloys