The effect of atmospheric corona treatment on AA1050 aluminium
Materials and Surface Engineering, Department of Mechanical Engineering, Technical University of Denmark1
Department of Mechanical Engineering, Technical University of Denmark2
Center for Electron Nanoscopy, Technical University of Denmark3
Surface Physics and Catalysis, Department of Physics, Technical University of Denmark4
Department of Physics, Technical University of Denmark5
The effect of atmospheric corona discharge on AM 050 aluminium surface was investigated using electrochemical polarization, SEM-EDX, FIB-SEM. and XPS. The corona treatment was performed with varying time (1, 5, and 15 min) in atmospheric air. A 200 nm oxide layer was generated on AA1050 after the 15 min air corona treatment.
A significant reduction in anodic and cathodic reactivities was observed starting from 1 min exposure, which further decreased with prolonged exposure (15 min) and after delayed testing (after 30 days). The reduction in surface reactivity is due to the formation of thicker and denser oxide film.
Language: | English |
---|---|
Year: | 2010 |
Pages: | 2155-2163 |
ISSN: | 18790496 and 0010938x |
Types: | Journal article |
DOI: | 10.1016/j.corsci.2010.01.035 |
ORCIDs: | Chorkendorff, Ib and Ambat, Rajan |